Rust-Oleum 9100 WG Winter Grade Low Temperature Epoxy

Two pack high performance epoxy system for metal, walls and floors. Winter Grade version.

• Pack Size: 4.5 litres

--

 

Rust-Oleum 9100 WG Winter Grade Low Temperature Epoxy

Two-pack epoxy system for high performance and maintenance. Winter Grade low temperature version of Rust-Oleum 9100. Also available in a High Solids version.

 

Product Description

Rust-Oleum 9100 Winter Grade Epoxy is a lower temperature version of the standard 9100 Epoxy.

A two-pack, gloss epoxy coating for metal, walls and floors. The most efficient epoxy system providing a very hard coating with high layer thickness for lasting results even with a single coat application. Ideal as a glossy floor paint for garages, warehouses, indoor car parks etc., with optimal protection achieved in only one or two applications.

 

Product Advantages

• 2 times thicker than regular epoxies (125 micron dry)

• Very resistant against abrasion and chemicals

• Contains a high amount of rust inhibitors

• Can be applied on metal and floors

• Tint-able in almost any colour

 

Recommended Use

9100 Topcoats are designed for application on manually prepared rusted steel surfaces and can also be used on clean, blasted steel, primed steel, concrete and previously coated
surfaces. 9100 Topcoats offer appropriate protection against strong chemicals, acids, alkalis and solvents; frequent product spillage and chemical cleaning; high humidity and moisture
conditions.

 

Recommended System

Primers: 9100 Topcoats can be applied on cleaned, sound mineral substrates, sound, well prepared previous coatings. Porous substrates should be primed with 5401 Impregnation Primer or 5421 Primer Rapid. Very dense substrates, such as ceramic tiles, should be primed with 3333 Super Adhesive Primer or 3366 Power Float Floor Primer.

Topcoat: If good U.V. resistance is required Polyurethane Topcoats 9200 Rust-O-Thane or 9600 should be applied (except for the clear coatings). 9100 Topcoats can be applied directly on 9170/9180 High Performance Metal Primers or 9169 Epoxy Rust Primer.

 

Surface Preparation

Remove grease, oil and all other surface contaminations by alkaline or high pressure (steam)cleaning in combination with appropriate detergents. Sand previous coatings which are in good condition to remove gloss and to roughen the surface slightly, check compatibility. The surface must be clean and dry during application.

Steel

Remove loose rust, mill scale and deteriorated coatings by hand or power tool cleaning to St 2/3 (ISO 8501-01 : 1988). Large areas may be brush-off blasted to Sa 2 (ISO 8501-01: 1988), blast profile max. 50 µm. For immersion purposes, prepare to Sa 3 (ISO 8501-01 :1988), blast profile max. 75 µm.

Concrete and masonry

New concrete or masonry should cure and dry for at least 30 days before applying the coating system. Remove laitance, any loose or unsound concrete or deteriorated coatings. Smooth concrete should be roughened.

 

Directions for Use

Base 9100 + Activator 9101: Standard grade
Base 9100 + Activator 9101HS: High Solids grade
Base 9100 + Activator 9101WG: Winter Grade, application at low temperature

Stir individual components thoroughly before mixing them together. Use a mechanical low speed mixer. Mix the product carefully for 3 minutes. Temperature of the mixed materials should be at least 10°C.

 

Application Conditions

Temperature of air and substrate between 10°C and 35°C (for the 9100/9101WG between 0 and 15°C) and relative humidity below 85%. The substrate temperature must be at least 3°C above dew-point.

 

Application and Thinning

Brush: Use natural bristles, long hair brushes. Dilute up to 10% volume with Thinner 160 (do not dilute 9101HS). Preferably use disposable brushes.

Roller: Use a medium nap polyamide 16-20 mm rollers. Roller application requires 2 coats to achieve recommended d.f.t. Dilute up to 10% volume with Thinner 160 (do not dilute 9101HS)
Preferably use disposable rollers.

Airless Spray: Tip size: 0.013-0.021 inch. Fluid pressure: 150 - 225 bar. Avoid excessive film thickness. Up to 10% volume Thinner 160 (do not dilute 9101HS).

Air-Atomised Spray: Not recommended.

 

Cleanup

Rust-Oleum Thinner 160.

 