PPG Hi-Temp 707 HB

Description

One component proprietary waterborne liquid insulation that provides thermal resistance and personnel protection up to 177°C
(350°F)

Principal Characteristics

 100% adherent, low permeability seamless composite insulation material
• Excellent for use as a personnel protection material, reducing burn injuries and reportable lost time accidents
• Used to prevent or reduce condensate formation
• Suitable for high build applications up to 1250 microns (50 mils) DFT per coat and up to 4 coats or 5000 microns (200
mils) for maximum thermal performance
• High film build capability in one single layer of 1250 microns (50.0 mils), reducing labor costs and increasing production
rates
• Suitable for applications at metal temperature up to 149°C (300°F)
• Able to withstand cyclic temperatures from -57°C (-70°F) to 177°C (350°F)
• Offers an economical alternative to conventional insulation and jacketing for process equipment and piping up to 177°C
(350°F)
• Superior energy savings due to its monolithic and adherent composite structure
• Easy visual inspection, facilitating future planning and remediation
• Used to control and stabilize process temperatures for storage tanks, pipelines, and vessels
• Ideal for varying geometric shapes, such as spheres, valves, and complex equipment
• Must always be used with the appropriate primers and topcoats. Refer to the system specification section for approved
product systems
• For non-immersion service ONLY; avoid use where standing or pooling water may develop

Colour and Gloss Level

• White
• Finish is textured to semi-smooth

Instructions For Use

 Store PPG HI-TEMP 707 HB in a dry place as close to room temperature as possible. Storage temperature should be
between 4°C to 38°C (40°F to 100°F). DO NOT ALLOW TO FREEZE
• When a container is first opened, PPG HI-TEMP 707 HB will normally have a dry, crumbly crust at the top of the container;
this crust may extend several centimeters (inches) down into the can. Beneath is a liquid layer
• Use only a screw auger mixer at slow speed or a 30" mud mixer. Mix until fully homogenized, See further mixing
instructions, refer to the PPG HI-TEMP 707 HB Application Guide
• When properly mixed, the consistency of PPG HI-TEMP 707 HB should be heavy-bodied (high viscosity) but free flowing,
and there should be few or no lumps
• PPG HI-TEMP 707 HB should be fully mixed without thinning. Any decision to thin the material should be made only after
fully mixing and observing the condition of the mixed material. If thinning is needed, add small amounts of tap water at a
time. Note: Adding water to PPG HI-TEMP 707 HB will reduce viscosity and will affect film build and the drying properties
of the product
• Mixed material may dry out and become unusable. Remixing may allow for reuse. Any material mixed and left uncovered
for 4 hours must be discarded

Notes:
- Do not apply if rain or heavy dew is anticipated before dry to recoat time is achieved
- Do not apply where sitting or pooling water may develop